The effects of water flow rate on shear bond strength of self etch resin cement to dentin surface after Er,Cr:YSGG laser etching

The aim of the present study was to evaluate the effect of water flow rate on the morphological features of dentin and shear bond strength (SBS) of self-etching resin cement after Er,Cr:YSGG laser etching. Dentin specimens obtained from extracted human third molars were randomly assigned to four groups (n = 23), including one that received no laser irradiation (control-group D) and three others with different laser parameters: 2.25 W, 50 Hz, 60% air with water flow rates of 19 mL/min-100% water (group A), 2.25 W, 50 Hz, 6.75 mL/min-50% water (group B), and 2.25 W, and 50 Hz, 2.75 mL/min-25% water (group C). The morphological features of each group were examined with scanning electron microscopy and atomic force microscopy. The SBS of resin cement disks (Panavia F2.0, Kuraray; Tokyo, Japan) (3 mm in diameter and 2 mm in height) to the dentin specimens was measured using a universal testing machine at a cross head speed of 0.5 mm/min. Bond strength values were analyzed with one-way ANOVA/Tukey tests. There were no significant differences between the SBS values of groups A and B (p > 0.05). However, the SBS values of these groups were significantly higher when compared to groups C and D (p < 0.001). Er,Cr:YSGG laser application with water flow rates of 6.75 or 19 mL/min resulted in better dentin surface alterations and increased the SBS of self-etching resin cement to dentin.