This study investigates the microstructure, electrical, corrosion, and mechanical properties of plate-shaped aluminum-copper couple produced using the explosive welding method. Mechanical tests, including hardness, tensile, tensile-shear, and impact test, concluded that the Al-Cu bimetal had an acceptable joint resistance. In this study, local intermetallic regions formed on the interface of the joint of the aluminumcopper bimetal, produced using the explosive welding technique. However, the formed intermetallic regions had no significant effect on the mechanical properties of the joint, except for increasing its hardness. According to electrical conductivity tests, the Al-Cu bimetal had an average electrical conductivity in comparison to the electrical conductivity of aluminum and copper, which were the original materials forming the joint. According to the results of electro-chemical corrosion test, during which galvanic corrosion formed, the Al side of the Al-Cu bimetal was more anodic due to its high electronegativity; as a result, it was exposed to more corrosion in comparison to the copper side. © ASM International.