The purpose of this study was to investigate the effects of mineral trioxide aggregate (MTA) on survival, mineralization, and expression of mineralization-related genes of cementoblasts. Immortalized cementoblasts (OCCM) were maintained with Dulbecco modified Eagle medium containing 10% fetal bovine serum. Methyl-thiazol-diphenyl-tetrazolium experiments were performed at 24 and 72 hours to evaluate bioactive components released by MTA (0.002-20 mg/mL) on the cell survival of OCCM. Von Kossa staining was used to evaluate biomineralization of OCCM cells. Images of cementoblasts were taken on day 3 by using inverted microscopy. Gene transcripts for bone sialoprotein (BSP), OCN, collagen type I (COL I), and osteopontin (OPN) were evaluated on days 3 and 5 by using semiquantitative reverse transcriptase polymerase chain reaction. The 20 mg/mL concentration of MTA was toxic for OCCM cells, whereas other concentrations of MTA tested exhibited similar cell numbers when compared with control group, and the 0.02 mg/mL concentration of MTA increased OCCM cell survival at 72 hours. Although an apparent decrease in mineralization was observed in the highest 3 concentrations of MTA used, 0.02 and 0.002 mg/mL concentrations of MTA induced greater biomineralization of OCCM cells than seen in the control. Moreover, increased BSP and COL I mRNA expression was observed at 0.02 and 0.002 mg/mL concentrations of MTA. MTA did not have a negative effect on the viability and morphology of cementoblasts and induced biomineralization of cementoblasts at the concentrations of 0.02 and 0.002 mg/mL. Based on these results MTA can be considered as a favorable material regarding cell-material interaction. © 2009 American Association of Endodontists.