AISI 5140 is a steel alloy used for manufacturing parts of medium speed and medium load such as gears and shafts mainly used in automotive applications. Parts made from AISI 5140 steel require machining processes such as turning and milling to achieve the final part shape. Limited research has been reported on the machining vibration and surface roughness during turning of AISI 5140 in the open literature. Therefore, the main aim of this paper is to conduct a systematic study to determine the optimum cutting conditions, analysis of vibration and surface roughness under different cutting speeds, feed rates and cutting edge angles using response surface methodology (RSM). Prediction models were developed and optimum turning parameters were obtained for averaged surface roughness (Ra) and three components of vibration (axial, radial and tangential) using RSM. The results demonstrated that the feed rate was the most affecting parameter in increasing the surface roughness (69.4%) and axial vibration (65.8%) while cutting edge angle and cutting speed were dominant on radial vibration (75.5%) and tangential vibration (64.7%), respectively. In order to obtain minimum vibration for all components and surface roughness, the optimum parameters were determined as Vc = 190 m/min, f = 0.06 mm/rev, Κ = 60° with high reliability (composite desirability = 90.5%). A good agreement between predicted and measured values was obtained with the developed model to predict surface roughness and vibration during turning of AISI 5140 within a 10% error range.