Ultrastructural correlates of in vivo/in vitro bond degradation in self-etch adhesives
Scopus
Toplam 125 atıf DOI
The morphologic correlates of bond degradation in self-etching primers have not been fully elucidated. We hypothesized that there is no difference between the mechanism of degradation of self-etching primers in vivo and in vitro. Class I cavities prepared in vivo in 24 caries-free human molars were bonded with Clearfil SE Bond or Clearfil Protect Bond, and restored with resin composites. Eight teeth were extracted after 24 hrs, and the rest after 1 yr. The same protocol was repeated in vitro with extracted molars. Degradation of resin-dentin bonds was assessed by microtensile bond testing and TEM of interfaces after tracer immersion. Both in vivo and in vitro bond strengths decreased with time for SE Bond but not for Protect Bond, with more pronounced water treeing observed in the former adhesive under both aging conditions. There is no difference between the mechanism of degradation of self-etch adhesives in vivo or in vitro.
Atıf Kaynağı
Atıf Yapan Yayın
Effects of remineralization procedures on shear bond strengths of brackets bonded to demineralized enamel surfaces with self-etch systems
Scopus
Havuzumuzda Open Access 22 atıf almış
Objective: To compare the effects of different remineralization procedures on the surface roughness of teeth, shear bond strengths (SBSs), and Adhesive Remnant Index scores of selfetching primer (SEP) used to bond orthodontic brackets to previously treated demineralized enamel surfaces. Materials and Methods: A total of 140 extracted human premolar teeth were randomly divided into seven equal groups. Group I was the control group. A demineralization procedure was performed in the other six groups. A remineralization procedure was performed before bonding by using casein phosphopeptide-amorphous calcium phosphate, fluoride, a microabrasion mixture (18% hydrochloric acid-fine pumice), a microabrasion agent, and resin infiltration in groups III to VII. Brackets were bonded using a self-etching primer/adhesive system. The specimens were tested for SBS. The roughness and morphology of the enamel surfaces were analyzed using profilometer and scanning electron microscopy. Data were analyzed with analysis of variance, Tukey, and G-tests at the a 5 .05 level. Results: Significant differences were found in the SBS values among the seven groups (F 5 32.69, P 5 .003). The lowest SBS value was found in group II (2.62 6 1.46 MPa). No significant differences were found between groups I, III, and VII, between groups III and IV, or between groups V and VI. The differences in the roughness values were statistically significant among the groups (P 5 .002). Conclusions: Remineralization procedures restore the decreased SBS of orthodontic brackets and decrease surface roughness caused by enamel demineralization. SEPs provide clinically acceptable SBS values for bonding orthodontic brackets to previously treated demineralized enamel surfaces.