Adsorption of Cu(II) from aqueous solution by using modified Fe3O4 magnetic nanoparticles
Scopus
Toplam 205 atıf DOI
In this study, surface modification of Fe3O4 nanoparticles (Fe3O4-NPs) was carried out with 3-aminopropyltriethoxysilane (APTES) and glutaraldehyde (GA). The obtained modified-NPs (GA-APTES-NPs) were evaluated for Cu(II) removal from water by adsorption. First, Fe3O4-NPs were synthesized by co-precipitation of Fe2+ and Fe3+ with Fe2+/Fe3+ in a ratio of 1.75 in an ammonia solution, then surface of Fe3O4-NPs was modified with APTES and GA. The morphology and properties of the NPs were examined by Transmission Electron Microscopy (TEM), Fourier Transform Infrared Spectroscopy (FT-IR), Thermal Gravimetric Analysis (TGA) and magnetization measurement. The batch experiments showed that modified-NPs can be effectively used to remove Cu(II) from water. Adsorption equilibrium was achieved in 15 min. The adsorption of Cu(II) by GA-APTES-NPs strongly depends on the pH of the solution. Maximum removal of Cu(II) was obtained at pH between 4.0 and 5.3. The isotherm analysis indicated that the sorption data can be represented by both Langmuir and Freundlich isotherm models. The regeneration studies also showed that GA-APTES-NPs could be re-used for the adsorption of Cu(II) from aqueous solutions over three cycles without change in the sorption capacity and magnetization properties. Crown Copyright © 2009.
Atıf Kaynağı
Atıf Yapan Yayın
A new BODIPY/nanoparticle/Ni affinity system for binding of cytochrome c
Scopus
Havuzumuzda 11 atıf almış
In this study, 3,5-{Bis[4,4-difluoro, 8-(2,6-diethyl, 1,3,5,7-tetramethyl-4-bora-3a,4a-diaza-s-indacene)]}benzoylchloride (BODIPY) was synthesized for the improving of a new immobilized metal affinity supporting material. Firstly, the synthesized BODIPY was immobilized on iron oxide superparamagnetic nanoparticles (SPIONs) and then, Ni(II) ions were chelated with the active terminals of BODIPY on nanoparticles surfaces to prepare an immobilized metal affinity (IMA) adsorbent for protein adsorption. The amount of BODIPY coated on SPIONs was about 29.7 μM at 10 mg nanoparticles. 738 μmol of Ni(II) ions were loaded to 10 mg of the SPIONs/BODIPY. The binding amount of cytochrome c was found to be 170 μg to the SPIONs/BODIPY/Ni at pH 7.4. The binding amount of the molecules on SPIONs was analyzed by using UV-vis, fluorescence and atomic absorption spectroscopy. The characterization of the prepared surfaces was performed by FT-IR, SEM and TEM.
Atıf Yapan Makale Bilgileri
Kurumlar (1)
Selçuk Üniversitesi
Selçuklu, Turkey